喷瓷管道及其焊接性能试验
Sprayed Porcelain Pipe and Test of Its Welding Performance
浏览(1793) 下载(2)
- DOI:
- 作者:
- 王勇
Wang yong
- 作者单位:
- 石油大学 257062 山东省东营市
Dongying, Shandong
- 关键词:
- 管道;防腐;管道焊接;陶瓷;防腐材料;热喷涂
Pipe line;Corrosion control;Pipeline welding;Ceramic;Corrosion prevention;Thermal spray
- 摘要:
- 本文报道喷瓷管道试件的焊接试验结果。试验表明,焊接电弧热会使喷瓷涂层发生重熔、开裂、剥落,焊接线能量越大影响越严重。只有选择合适的焊接线能量才可使喷瓷涂层发生重熔,得到表面无裂纹的接头。此外,喷瓷管道焊接热影响区的金属基体将由于喷瓷过程中渗入的固溶氮而产生大量微裂纹。
This paper provides welding test result of specimen of sprayed porcelain pipe. The result showes that thermal of welding electic arc can make the sprayed porcelain layer re-melt, crack and split. The more welding line energy is, the more serious damages are. To select proper welding line energy is the only way to make the layer re-melt only and to gain a pipe joint without crack on its surface. In addition, the metal body within welding heat effect zone will produce a lot of micro-cracks because of infiltration of solid solution nitrogen in course of porcelain spraying.1997,5(5): 12-13 收稿日期：1997-1-21基金项目：山东省自然科学基金资助项目.代号Y95F0376参考文献：
1 喻家庆.在碳钢基材上激光熔覆玻璃涂层及其物理化学行为研究.腐蚀科学与防腐技术，1995;7 (1)
2 张亚平，高家诚.热障陶瓷基复合涂层的组织和性能.机械工程材料，1993; 17 (4)
3 肖宏滨，王庆丰等.陶瓷材料的火焰喷涂.新技术新工艺，1995;(5)
4 吴秋红，陶曾毅等.不锈钢表面热喷涂陶瓷的激光重熔组织及成分分布.机械工程材料，1995; 19 (1)
5 邵文右，王理泉.中华人民共和国发明专利，CN 105I075A