江苏LNG项目16万m~3储罐海水试压方法探究及实践
Investigation and Practice of Hydrostatic Test by Using Seawater for 160 000 m~3 Tank in Jiangsu LNG Project
浏览(2111) 下载(6)
- DOI:
- 作者:
- 洪宁1, 刘洪亮2, 胡本源1
HONG Ning1
- 作者单位:
- 1.中石油江苏液化天然气有限公司 江苏南通 226001;
2.中国石油管道学院 河北廊坊 065000
PetroChina Jiangsu LNG Co., Ltd., Nantong 226001, China
- 关键词:
- LNG储罐;海水试压;阴极保护措施;腐蚀
LNG tank;hydrostatic test by using seawater;catholic protection measure;corrosion
- 摘要:
- LNG储罐水压试验采用海水作为试验介质时，海水对内罐9%Ni钢材的腐蚀性是需要考虑的问题。江苏LNG项目16万m3储罐内罐材质为9%Ni钢，通过9%Ni钢试板(分母材试板和带焊缝试板)在海水中长达30d的腐蚀试验，证明在较短时间内海水对内罐的腐蚀很小，因此尝试了内罐采用海水试压并且不采取阴极保护措施的做法，获得成功。
When using seawater as the medium to carry out hydrostatic test of LNG tanks,the corrosiveness of seawater to Ni9% steel must be considered.In Jiangsu LNG Project,the inner tank of a 160 000 m 3 LNG tank is made of Ni9% steel.The corrosion tests by putting 9%Ni steel test plates(including nine mother metal plates and one welded plate) into seawater for 30 days prove that the corrosion of seawater to inner tank is very weak.So that cathodic protection measure is not needed in the inner tank hydrostatic test by using seawater,and the hydrostatic test achieves success.2013,4(4): 46-48 收稿日期：2013-4-1DOI：10.3969/j.issn.1001-2206.2013.04.013作者简介：洪宁(1972-)，男，江苏南京人，工程师，1991年毕业于洛阳石油技工学校，现从事石油天然气地面工程建设工作。参考文献：