N80油套管在油田采出液中的腐蚀与磨损协同作用研究
Investigation on Associated Actions of Corrosion and Abrasion of N80 Casing Pipe in Oilfield Produced Liquid
浏览(2096) 下载(2)
- DOI:
- 作者:
- 李金波1,2, 舒欣欣1, 郑茂盛2
LI Jin-bo1,2, Shu Xingxing1, Zhang Maosheng2
- 作者单位:
- 1. 西安交通大学材料科学与工程学院, 陕西西安 710049;
2. 西北大学凝聚态物理与材料研究所, 陕西西安 710069
Collage of Material Science and Engineering, Xi'an Jiaotong University, Xi'an 710069, China
- 关键词:
- 油套管;动静态腐蚀;腐蚀磨损;协同作用
oil casing pipe;dynamic and static corrosions;corrosive abrasion;associated action
- 摘要:
- 以长庆油田分公司樊家川油田采出液为介质，在自制的腐蚀磨损试验机中对比研究了N80油套管钢在其中的动静态腐蚀、腐蚀磨损以及缓蚀剂对腐蚀磨损（自行研发的NYS-9缓蚀剂）的协同作用。结果表明，在动态试验中，腐蚀产物膜在流体剪应力的作用下，使得N80油套管钢的局部腐蚀比静态试验严重得多；腐蚀磨损试验初期腐蚀磨损速率较大，随后逐渐减缓；NYS-9缓蚀剂对N80油套管钢具有很好的保护作用，加入缓蚀剂的质量分数为100×10-6时，缓蚀率可达到82%以上。
The dynamic and static corrosions, corrosive abrasion, and the associated effect of corrosion inhibitor (NYS-9 type, developed by oneself ) on corrosive abrasion are investigated putting N80 casing pipe steel into a homemade corrosive abrasion test machine filled with produced liquid came from Fanjiachuan Oilfield of Changqing Oilfield. The test results show that local corrosion of N80 steel are more severe in dynamic test than in static test owing to the action of fluid shearing stress on produced corrosive membrane; the corrosive abrasion rate at primary stage is rather high, and retards gradually afterwards; NYS-9 corrosion inhibitor has an effective protection function to N80 casing pipe steel, retarding rate above 82% with 100ppm concentration of corrosion inhibitor.2007,2(2): 26-30 收稿日期：2006-6-27分类号：TE931.2作者简介：李金波（1966- ），男，湖北荆州人。西安交通大学材料科学与工程学院博士，主要从事油套管的腐蚀损伤及防护技术研究。参考文献：
[1] Ann S S.Wear behavior of some lowalloy steels under combined impact/abrasion contact conditions [J]. Wear,2001,250:744-754.
[2] McLauy B S,Wang J,Shirazi S A,et al.HowOperating and EnvironmentalConditions Affect Erosion [C].CORROSION/99,Paper No.034,NACE (international) 1999.
[3] Lazt U.Velocity Effects in FlowInduced Corrosion[C].CORROSION/90,Paper No. 090,NACE,1990.
[4] Chakraborty I,Basak A,Charrerjee U K. Corrosive wear behavior ofCr -Mn -Cu white cast irons in sand -water slurry media [J].Wear,1991,143(3):203-220.
[5] KimKY.Wear ofMaterials[M].1981:112.
[6] 李诗卓,董祥林. 材料的冲蚀磨损与微动磨损[M].北京:机械工业出版社,1987.
[7] 路新春,张天成,李诗卓,等.三种腐蚀磨损试验机与两种不锈钢腐蚀磨损性能的研究[J].摩擦学学报,1994,14(2):97-104.
[8] Madsen B W. Standard guide for determining amount of synergism between wear and corrosion [A].ASME G119 -93,1994 Ann.Book ASTM Stand.,Vol.03.02,Wear and Erosion,Metal Corrosion [C]. Philadelphia,PA:ASTM,1994:507-512.
[9] 林冠发,郑茂盛,白真权,等. N80钢CO2腐蚀产物膜在水/ 砂两相流介质中的磨损性能[J].摩擦学学报,2005,25(1):78-82.
[10] 林玉珍. 流动条件下腐蚀磨损的研究进展[J].全面腐蚀控制,1996,10(4):1-3.