热采锅炉炉管接头失效分析
Failure Analysis of Furnace Tube Joint in Thermal Recovery Boiler
浏览(2235) 下载(2)
- DOI:
- 作者:
- 岳峰1, 何艳玲2, 何长1, 赵为民2
YUE Feng1
- 作者单位:
- 1. 中国石化胜利油田分公司孤岛采油厂, 山东东营 257231;
2. 中国石油大学机电学院 山东东营 257061
SINOPEC Shengli Oilfield Gudao Petroleum Production Plant, Dongying 257231, China
- 关键词:
- 热采锅炉;炉管;接头;失效分析
thermal recovery boiler;furnace tube;welded joint;failure analysis
- 摘要:
- 某热采锅炉投入使用不到一年,其炉管焊接接头就发生失效,通过宏观观察、化学成分和微观组织分析、断口形貌扫描电镜观察以及焊接接头硬度分布测试,对早期失效原因进行了分析。结果表明:接头反面成型出现焊瘤,近缝区出现魏氏体过热组织,裂纹沿熔合区或过热区扩展,打底焊缝和盖面焊缝组织不均匀,打底焊位置接头的硬度分布不均匀性明显高于盖面焊缝。打底焊采用的热输入太大是炉管早期失效的根本原因。
Several furnace tube joints in a thermal recovery boiler failed shortly after being put into use. Failure analysis was carried out using microscopy, SEM and chemical composition analysis instrument together with testing the distribution of hardness in welded joints. The results show that there are overlaps on back bead and overheated structure such as Widmanstaten structure in the zone near the weld, and cracks propagate along the fusion zone or overheated zone. The distribution of hardness across backing bead is non-uniform comparing with that across other beads. Therefore, it can be concluded that it is the too big heat input applied to the back bead that induces the failure of the tube joints.2008,3(3): 51-52,71 收稿日期：2007-10-12分类号：TK229作者简介：岳峰（1968-），男，山东临沂人，工程师，1994年毕业于承德石油高等专科学校热能工程专业，长期从事热能工程专业工作.参考文献：
[1]李金林,于鹭.稠油废水回用热采锅炉供水工艺与工程实践[J].工业水处理,2005,26(5):87-90.
[2]王艳芳.稠油热采锅炉结垢物的X射线衍射分析[J].科学技术与工程.2006,18(6):2934-2937.
[3]金相图谱编写组.金相图谱[M].北京:电力工业出版社,1980.206-209.
[4]刘永铨.钢的热处理[M].北京:冶金出版社,1979.39-45.
[5]温涛,卢鑫,温建萍.高压热采锅炉炉管的腐蚀与安全性分析[J].压力容器,2004,21(10):47-50.
[6]温涛,张乃峰,卢鑫,等.热采锅炉炉管爆裂原因分析[J].金属热处理,2004,29(11):57-59.